Klasifikasyon pou chak metòd pwodiksyon
● san pwoblèm
● Soude
Klasifikasyon pou chak metòd soude
● Erw
● Sawl
● Ssaw
Dimansyon gwosè
Lèt | OD | Epesè |
San pwoblèm | Ø33.4-323.9mm (1-12 nan) | 4.5-55mm |
ERW | Ø21.3-609.6mm (1/2-24 nan) | 8-50mm |
Sawl | Ø457.2-1422.4mm (16-56 nan) | 8-50mm |
Ssaw | Ø219.1-3500mm (8-137.8 nan) | 6-25.4mm |
Klas ekivalan
Estanda | Egalize | |||||||||
API 5L | A25 | Gr a | GRB | X42 | X46 | X52 | X56 | 60 | 65 | 70 |
GB/T 9711 ISO 3183 | L175 | L210 | L245 | L290 | L320 | L360 | L390 | L415 | L450 | L485 |
Konpozisyon chimik
Konpozisyon Chimik pou PSL 1 tiyo ak t ≤ 0.984 "
Klas asye | Fraksyon mas, % ki baze sou chalè ak pwodwi analyses a, g | |||||||
C | Mn | P | S | V | Nb | Ti | ||
max b | max b | max | max | max | max | max | ||
Tiyo san pwoblèm | ||||||||
A | 0.22 | 0.9 | 0.3 | 0.3 | - | - | - | |
B | 0.28 | 1.2 | 0.3 | 0.3 | c, d | c, d | d | |
X42 | 0.28 | 1.3 | 0.3 | 0.3 | d | d | d | |
X46 | 0.28 | 1.4 | 0.3 | 0.3 | d | d | d | |
X52 | 0.28 | 1.4 | 0.3 | 0.3 | d | d | d | |
X56 | 0.28 | 1.4 | 0.3 | 0.3 | d | d | d | |
X60 | 0.28 E | 1.40 E | 0.3 | 0.3 | f | f | f | |
X65 | 0.28 E | 1.40 E | 0.3 | 0.3 | f | f | f | |
X70 | 0.28 E | 1.40 E | 0.3 | 0.3 | f | f | f | |
Tiyo soude | ||||||||
A | 0.22 | 0.9 | 0.3 | 0.3 | - | - | - | |
B | 0.26 | 1.2 | 0.3 | 0.3 | c, d | c, d | d | |
X42 | 0.26 | 1.3 | 0.3 | 0.3 | d | d | d | |
X46 | 0.26 | 1.4 | 0.3 | 0.3 | d | d | d | |
X52 | 0.26 | 1.4 | 0.3 | 0.3 | d | d | d | |
X56 | 0.26 | 1.4 | 0.3 | 0.3 | d | d | d | |
X60 | 0.26 E | 1.40 E | 0.3 | 0.3 | f | f | f | |
X65 | 0.26 E | 1.45 E | 0.3 | 0.3 | f | f | f | |
X70 | 0.26E | 1.65 E | 0.3 | 0.3 | f | f | f |
a. Cu ≤ = 0.50% Ni; ≤ 0.50%; Cr ≤ 0.50%; ak mo ≤ 0.15%,
b. Pou chak rediksyon nan 0.01% anba a konsantrasyon an maksimòm espesifye pou kabòn, yon ogmantasyon de 0.05% pi wo a konsantrasyon an maksimòm espesifye pou MN se akseptab, jiska yon maksimòm de 1.65% pou klas ≥ L245 oswa B, men ≤ L360 oswa X52; jiska yon maksimòm de 1.75% pou klas> L360 oswa X52, men <L485 oswa X70; ak jiska yon maksimòm de 2.00% pou klas L485 oswa x70.,
c. Sòf si otreman te dakò NB + V ≤ 0.06%,
d. Nb + v + ti ≤ 0.15%,
e. Sof si otreman te dakò.,
f. Sòf si otreman te dakò, nb + v = ti ≤ 0.15%,
g. Pa gen okenn adisyon ekspre nan B pèmèt ak rezidyèl B ≤ 0.001%
Konpozisyon chimik pou PSL 2 tiyo ak t ≤ 0.984
Klas asye | Mass fraksyon, % ki baze sou chalè ak pwodwi analyses | Ekivalan kabòn | |||||||||
C | Si | Mn | P | S | V | Nb | Ti | Lòt | CE IIW | CE PCM | |
max b | max | max b | max | max | max | max | max | max | max | ||
Tiyo san pwoblèm | |||||||||||
BR | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | c | c | 0.04 | e, l | 0.43 | 0.25 |
X42R | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | 0.06 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
BN | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | c | c | 0.04 | e, l | 0.43 | 0.25 |
X42n | 0.24 | 0.4 | 1.2 | 0.025 | 0.015 | 0.06 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X46n | 0.24 | 0.4 | 1.4 | 0.025 | 0.015 | 0.07 | 0.05 | 0.04 | d, e, l | 0.43 | 0.25 |
X52n | 0.24 | 0.45 | 1.4 | 0.025 | 0.015 | 0.1 | 0.05 | 0.04 | d, e, l | 0.43 | 0.25 |
X56n | 0.24 | 0.45 | 1.4 | 0.025 | 0.015 | 0.10f | 0.05 | 0.04 | d, e, l | 0.43 | 0.25 |
X60n | 0.24F | 0.45F | 1.40f | 0.025 | 0.015 | 0.10f | 0.05f | 0.04F | g, h, l | Kòm te dakò | |
BQ | 0.18 | 0.45 | 1.4 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X42Q | 0.18 | 0.45 | 1.4 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X46q | 0.18 | 0.45 | 1.4 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X52Q | 0.18 | 0.45 | 1.5 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X56q | 0.18 | 0.45F | 1.5 | 0.025 | 0.015 | 0.07 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X60Q | 0.18f | 0.45F | 1.70f | 0.025 | 0.015 | g | g | g | h, l | 0.43 | 0.25 |
X65q | 0.18f | 0.45F | 1.70f | 0.025 | 0.015 | g | g | g | h, l | 0.43 | 0.25 |
X70Q | 0.18f | 0.45F | 1.80f | 0.025 | 0.015 | g | g | g | h, l | 0.43 | 0.25 |
X80Q | 0.18f | 0.45F | 1.90f | 0.025 | 0.015 | g | g | g | mwen, j | Kòm te dakò | |
X90Q | 0.16f | 0.45F | 1.9 | 0.02 | 0.01 | g | g | g | j, k | Kòm te dakò | |
X100Q | 0.16f | 0.45F | 1.9 | 0.02 | 0.01 | g | g | g | j, k | Kòm te dakò | |
Tiyo soude | |||||||||||
BM | 0.22 | 0.45 | 1.2 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X42m | 0.22 | 0.45 | 1.3 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X46m | 0.22 | 0.45 | 1.3 | 0.025 | 0.015 | 0.05 | 0.05 | 0.04 | e, l | 0.43 | 0.25 |
X52m | 0.22 | 0.45 | 1.4 | 0.025 | 0.015 | d | d | d | e, l | 0.43 | 0.25 |
X56m | 0.22 | 0.45F | 1.4 | 0.025 | 0.015 | d | d | d | e, l | 0.43 | 0.25 |
X60m | 0.12f | 0.45F | 1.60f | 0.025 | 0.015 | g | g | g | h, l | 0.43 | 0.25 |
X65m | 0.12f | 0.45F | 1.60f | 0.025 | 0.015 | g | g | g | h, l | 0.43 | 0.25 |
X70m | 0.12f | 0.45F | 1.70f | 0.025 | 0.015 | g | g | g | h, l | 0.43 | 0.25 |
X80m | 0.12f | 0.45F | 1.85f | 0.025 | 0.015 | g | g | g | mwen, j | .043f | 0.25 |
X90m | 0.1 | 0.55F | 2.10f | 0.02 | 0.01 | g | g | g | mwen, j | - | 0.25 |
X100m | 0.1 | 0.55F | 2.10f | 0.02 | 0.01 | g | g | g | mwen, j | - | 0.25 |
a. SMLS T> 0.787 ", limit CE yo dwe jan yo te dakò. Limit yo CEIIW aplike fi c> 0.12% ak limit yo CEPCM aplike si c ≤ 0.12%,
b. Pou chak rediksyon nan 0.01% anba a maksimòm ki espesifye pou C, yon ogmantasyon de 0.05% pi wo a maksimòm ki espesifye pou MN se akseptab, jiska yon maksimòm de 1.65% pou klas ≥ L245 oswa B, men ≤ L360 oswa X52; jiska yon maksimòm de 1.75% pou klas> L360 oswa X52, men <L485 oswa X70; jiska yon maksimòm de 2.00% pou klas ≥ L485 oswa X70, men ≤ L555 oswa x80; ak jiska yon maksimòm de 2.20% pou klas> L555 oswa x80.,
c. Sof si otreman te dakò nb = v ≤ 0.06%,
d. Nb = v = ti ≤ 0.15%,
e. Sòf si otreman te dakò, CU ≤ 0.50%; Ni ≤ 0.30% Cr ≤ 0.30% ak Mo ≤ 0.15%,
f. Sof si otreman te dakò,
g. Sòf si otreman te dakò, NB + V + Ti ≤ 0.15%,
h. Sòf si otreman te dakò, Cu ≤ 0.50% Ni ≤ 0.50% Cr ≤ 0.50% ak Mo ≤ 0.50%,
mwen. Sòf si otreman te dakò, Cu ≤ 0.50% Ni ≤ 1.00% Cr ≤ 0.50% ak Mo ≤ 0.50%,
j. B ≤ 0.004%,
k. Sòf si otreman te dakò, Cu ≤ 0.50% Ni ≤ 1.00% Cr ≤ 0.55% ak MO ≤ 0.80%,
l. Pou tout klas PSL 2 tiyo eksepte klas sa yo ak Footnotes J te note, sa ki annapre yo aplike. Sòf si otreman te dakò pa gen okenn adisyon entansyonèl nan B pèmèt ak rezidyèl B ≤ 0.001%.
Pwopriyete mekanik nan API 5L
Kondisyon pou rezilta yo nan tès rupture pou PSL 1 tiyo
Klas tiyo | Sede fòs yon | Fòs rupture a | Elongasyon | Fòs rupture b |
RT0,5 psi min | Rm psi min | (nan 2in af % min) | Rm psi min | |
A | 30,500 | 48,600 | c | 48,600 |
B | 35,500 | 60,200 | c | 60,200 |
X42 | 42,100 | 60,200 | c | 60,200 |
X46 | 46,400 | 63,100 | c | 63,100 |
X52 | 52,200 | 66,700 | c | 66,700 |
X56 | 56,600 | 71,100 | c | 71,100 |
X60 | 60,200 | 75,400 | c | 75,400 |
X65 | 65,300 | 77,500 | c | 77,500 |
X70 | 70,300 | 82,700 | c | 82,700 |
a. Pou klas entèmedyè, diferans ki genyen ant fòs la espesifye minimòm rupture ak sede a espesifye minimòm pou kò a tiyo yo dwe jan yo bay pou pwochen klas la pi wo. | ||||
b. Pou klas yo entèmedyè, espesifye minimòm fòs la rupture pou Couture a Weld yo dwe menm jan an jan yo detèmine pou kò a lè l sèvi avèk pye nòt a. | ||||
c. Pwolonjman minimòm espesifye a, AF, ki eksprime nan pousan ak awondi nan pousan ki pi pre a, yo dwe detèmine lè l sèvi avèk ekwasyon sa a: | ||||
Ki kote C se 1 940 pou kalkil lè l sèvi avèk inite SI ak 625 000 pou kalkil lè l sèvi avèk inite USC | ||||
AXC se moso nan tès ki aplikab rupture zòn kwa-rejyonal, ki eksprime nan milimèt kare (pous kare), jan sa a | ||||
-pou sikilè kwa-seksyon tès moso, 130mm2 (0.20 IN2) pou 12.7 mm (0.500 nan) ak 8.9 mm (.350 nan) dyamèt tès moso; ak 65 mm2 (0.10 IN2) pou 6.4 mm (0.250in) moso tès dyamèt. | ||||
-Pou moso tès konplè-seksyon, pi piti a nan A) 485 mm2 (0.75 IN2) ak b) zòn nan kwa-rejyonal nan moso nan tès, sòti lè l sèvi avèk dyamèt la espesifye deyò ak epesè nan miray espesifye nan tiyo a, awondi nan 10 mm2 ki pi pre a (0.10in2) | ||||
-Pou moso tès dezabiye, pi piti a nan A) 485 mm2 (0.75 IN2) ak b) zòn nan kwa-rejyonal nan moso nan tès, sòti lè l sèvi avèk lajè a espesifye nan moso nan tès ak epesè a miray espesifye nan tiyo a, awondi nan 10 mm2 ki pi pre a (0.10in2) | ||||
U se espesifye minimòm fòs la rupture, ki eksprime nan megapascals (liv pou chak pous kare) |
Kondisyon pou rezilta yo nan tès rupture pou PSL 2 tiyo
Klas tiyo | Sede fòs yon | Fòs rupture a | Rapò a, c | Elongasyon | Fòs rupture d | ||
RT0,5 psi min | Rm psi min | R10,5irm | (nan 2in) | RM (psi) | |||
Minimòm | Maksimòm | Minimòm | Maksimòm | Maksimòm | Minimòm | Minimòm | |
BR, BN, BQ, BM | 35,500 | 65,300 | 60,200 | 95,000 | 0.93 | f | 60,200 |
X42, x42r, x2q, x42m | 42,100 | 71,800 | 60,200 | 95,000 | 0.93 | f | 60,200 |
X46n, x46q, x46m | 46,400 | 76,100 | 63,100 | 95,000 | 0.93 | f | 63,100 |
X52N, x52Q, x52m | 52,200 | 76,900 | 66,700 | 110,200 | 0.93 | f | 66,700 |
X56N, x56q, x56m | 56,600 | 79,000 | 71,100 | 110,200 | 0.93 | f | 71,100 |
X60N, X60Q, S60M | 60,200 | 81,900 | 75,400 | 110,200 | 0.93 | f | 75,400 |
X65q, x65m | 65,300 | 87,000 | 77,600 | 110,200 | 0.93 | f | 76,600 |
X70Q, x65m | 70,300 | 92,100 | 82,700 | 110,200 | 0.93 | f | 82,700 |
X80Q, x80m | 80, .500 | 102,300 | 90,600 | 119,700 | 0.93 | f | 90,600 |
a. Pou klas entèmedyè, al gade nan spesifikasyon an plen API5L. | |||||||
b. Pou klas> x90, al gade nan spesifikasyon an plen API5L. | |||||||
c. Limit sa a aplike pou pi ak d> 12.750 nan | |||||||
d. Pou klas entèmedyè, espesifye fòs la minimòm rupture pou Couture a Weld yo dwe menm valè a jan yo te detèmine pou kò a tiyo lè l sèvi avèk pye a. | |||||||
e. Pou tiyo ki egzije tès Longitudinal, fòs la sede maksimòm yo dwe ≤ 71,800 psi | |||||||
f. Pwolonjman minimòm espesifye a, AF, ki eksprime nan pousan ak awondi nan pousan ki pi pre a, yo dwe detèmine lè l sèvi avèk ekwasyon sa a: | |||||||
Ki kote C se 1 940 pou kalkil lè l sèvi avèk inite SI ak 625 000 pou kalkil lè l sèvi avèk inite USC | |||||||
AXC se moso nan tès ki aplikab rupture zòn kwa-rejyonal, ki eksprime nan milimèt kare (pous kare), jan sa a | |||||||
-pou sikilè kwa-seksyon tès moso, 130mm2 (0.20 IN2) pou 12.7 mm (0.500 nan) ak 8.9 mm (.350 nan) dyamèt tès moso; ak 65 mm2 (0.10 IN2) pou 6.4 mm (0.250in) moso tès dyamèt. | |||||||
-Pou moso tès konplè-seksyon, pi piti a nan A) 485 mm2 (0.75 IN2) ak b) zòn nan kwa-rejyonal nan moso nan tès, sòti lè l sèvi avèk dyamèt la espesifye deyò ak epesè nan miray espesifye nan tiyo a, awondi nan 10 mm2 ki pi pre a (0.10in2) | |||||||
-Pou moso tès dezabiye, pi piti a nan A) 485 mm2 (0.75 IN2) ak b) zòn nan kwa-rejyonal nan moso nan tès, sòti lè l sèvi avèk lajè a espesifye nan moso nan tès ak epesè a miray espesifye nan tiyo a, awondi nan 10 mm2 ki pi pre a (0.10in2) | |||||||
U se espesifye fòs la minimòm rupture, ki eksprime nan megapascals (liv pou chak pous kare | |||||||
g. Pi ba valè fo r10,5irm ka espesifye nan akò | |||||||
h. Pou klas> x90, al gade nan spesifikasyon an plen API5L. |
Aplikasyon
Se tiyo a liy itilize pou transpò nan dlo, lwil oliv, ak gaz pou petwòl ak endistri gaz natirèl.
Jindalai Steel bay kalifye tiyo ki kalifye ak soude liy dapre Standand nan API 5L, ISO 3183, ak GB/T 9711.
Detay Desen


-
A106 Crosshole Sonic Logging Tib
-
API 5L Klas B tiyo
-
ASTM A106 Klas B tiyo san pwoblèm
-
A106 GRB tiyo asye san pwoblèm pou pil pou pil
-
ASTM A53 Crosshole Sonic Logging (CSL) soude tiyo
-
Ssaw asye tiyo/espiral soude tiyo
-
4140 Alloy Steel Tib & AISI 4140 tiyo
-
Gwo tiyo asye presizyon
-
ASME SA192 tiyo chofaj/A192 tiyo asye san pwoblèm
-
SA210 san pwoblèm asye chofaj tib